Preparation of methanol from synthesis gas with promoted palladium catalysts

ABSTRACT

An improved catalytic process for the production of methanol from hydrogen and carbon monoxide at a temperature of from about 200 DEG C. to about 400 DEG  C. and a pressure of from about 150 to about 20,000 psia which comprises effecting the reaction in the presence of a heterogeneous solid catalyst comprising palladium in combination with a metal additive selected from the group consisting of lithium, magnesium, strontium, barium, molybdenum and mixtures thereof.

CROSS-REFERENCE TO RELATED APPLICATION

This application is related to copending U.S. application Ser. No. 105,408 filed on even date herewith which describes a process for producing methanol from synthesis gas using a catalyst containing palladium and calcium.

BACKGROUND OF THE INVENTION

This invention relates, in general, to a catalytic process for producing methanol from synthesis gas. More particularly, the invention concerns reacting synthesis gas in the presence of a promoted palladium catalyst to form methanol at high carbon efficiencies and improved rates of production.

Methanol is an increasingly important feedstock for the production of carbon-based chemicals. Existing or proposed commercial processes using methanol include dehydrogenation to form formaldehyde, carbonylation to form acetic acid, homologation to form ethanol and reactions over zeolitic materials to form gasoline-grade fractions. The presently anticipated increase in commercial methanol manufacture has underscored the need for new and improved catalysts characterized by high carbon efficiencies and good productivity to methanol.

The use of catalysts to influence the product distribution resulting from the hydrogenation of carbon monoxide is well known in the art. Among the vast array of products obtainable from the reaction of carbon monoxide and hydrogen, methane is thermodynamically the most favored, longer chain hydrocarbons are next followed by high molecular weight alcohols with methanol being thermodynamically one of the least stable products which can be formed. Hence, specific catalysts for methanol synthesis are required in order to selectively produce methanol at high reaction efficiencies from synthesis gas. The prevalent commercial catalysts today for methanol manufacture from a synthesis gas are composed of oxides and mixed oxides of chromium, zinc and copper.

Palladium is also known in the art as an effective methanol catalyst. U.S. Pat. No. 4,119,656 to Poutsma et al., dated Oct. 10, 1978, discloses the formation of hydroxylated hydrocarbons such as methanol and ethylene glycol from synthesis gas in the presence of a palladium catalyst. While the process of Poutsma et al is characterized by very high selectivities of methanol, generally above 95 percent, the productivity of methanol is substantially below that achieved in commercial methanol synthesis processes. Hence, it would be desirable to significantly improve the methanol production rate of the Poutsma et al process while maintaining its high process efficiency.

SUMMARY OF THE INVENTION

This invention describes a catalyst for the production of methanol from the reaction of carbon monoxide and hydrogen, such catalyst being an improvement of that disclosed in the aforementioned U.S. Pat. No. 4,119,656. The process of the invention involves contacting a heterogeneous solid catalyst comprising palladium in combination with an effective amount of a metal additive selected from the group consisting of lithium, magnesium, strontium, barium, molybdenum and mixtures of same with synthesis gas comprising carbon monoxide and hydrogen at a temperature of from about 200° C. to about 400° C. and a pressure of from about 150 to about 20,000 psia to selectively form methanol.

The preferred reaction conditions are a temperature between about 250° C. and about 350° C. and a pressure between about 150 and about 3,000 psia.

The present invention is predicated on the discovery that the production rate of methanol in the aforementioned Poutsma et al process can be significantly enhanced by the addition of a metal promoter or additive as herein described to a palladium catalyst such as utilized in the Poutsma et al process. Thus, up to a three-fold increase in methanol manufacture can be achieved in accordance with the invention relative to the process of U.S. Pat. No. 4,119,656 without adversely affecting the very high process efficiencies achieved with such process.

PROCESS DISCUSSION

In accordance with the invention, a synthesis gas containing carbon monoxide and hydrogen is contacted with a palladium catalyst containing one or more of the aforementioned metal promoters under reaction conditions of temperature and pressure which thermodynamically favor the formation of methanol relative to hydrocarbons, such as, methane. The selectivity of the reaction to methanol is generally at least 90 percent, more typically about 95 percent or greater, and under preferred reaction conditions about 98 percent.

Molybdenum is the preferred metal promoter insofar as methanol production is concerned, albeit less preferred than lithium, magnesium, strontium and/or barium with regard to reaction efficiency to methanol. That is, the use of molybdenum in conjunction with palladium results in a significant increase in the manufacture of reaction products which although comprised primarily of methanol also include methane, two or more carbon atom hydrocarbons, and hydroxylated compounds, such as, ethanol. In contrast thereto, the use of lithium, magnesium, strontium and/or barium in accordance with the invention results in a generally higher reaction selectivity to methanol, typically above 95%, and under preferred reaction conditions about 98%, but a lower reaction productivity relative to the use of molybdenum.

Reaction selectivity, or efficiency, is defined herein as the percentage of carbon atoms converted from carbon monoxide to a specified compound other than CO₂.

The promoted palladium catalyst of the invention comprises palladium in combination with one or more of the aforementioned metal additives employed in a fine dispersion or slurried in a high boiling point solvent, or alternatively, supported upon an inert carrier material. The preferred mode of operation is to support the palladium catalyst and the desired metal additive(s) on a particulate high surface area support and the supported combination then placed into the reaction zone. In an alternate embodiment of the invention, the desired amount of metal additive is incorporated into the support during formulation so as to be an integral part of the finished support, the palladium being thereafter deposited upon such support. If desired, a portion of the metal additive may be incorporated into the support and the remainder deposited upon the support with the palladium catalyst.

A support having a surface area greater than 1.0 square meters per gram (BET low temperature nitrogen adsorption isotherm method) is generally preferred, a surface area above 10 square meters per gram being particularly desirable, although surface area is not the sole determinative variable. Silica gel is a preferred catalyst support with alpha alumina, gamma alumina, magnesia, carbon, zirconia and titania being among the useful albeit less desirable catalyst supports.

For the purpose of this invention it is believed that palladium deposited on particles of a compound of one or more of the aforementioned metal additives such as the oxide or carbonate is substantially the same as palladium and such additive(s) deposited on any of the above support materials.

On the basis of experience to date, the amount of palladium on the support should range from about 0.1 wt. % to about 20 wt. %, based on the weight of the support material. Preferably, the amount of palladium is within the range of about 2 to about 5 weight percent. The amount of metal additive in the catalyst may vary depending upon the particular metal additive, the catalyst support employed and the method of catalyst preparation. For a given additive, catalyst support, and method of catalyst preparation, the optimum concentration of additive is readily determined by simple experimentation. For additives such as lithium, magnesium, strontium and/or barium supported on a silica gel support, the preferred concentration of additive is from about 0.05% to about 1% by weight of the catalyst support. For molybdenum, concentrations of from about 0.1 to 5.0% by weight of the support are suitable with concentrations of from about 0.2 to 3.0% by weight being preferred.

Palladium and one or more of the aforementioned additives may be deposited onto the catalyst base or support by any of the commonly accepted techniques for catalyst preparation, as for example, impregnation from a solution containing the salts of palladium and the desired metal additive(s), precipitation, coprecipitation, or ion exchange. Typically, a solution of heat decomposable inorganic or organic palladium compound and a compound of lithium, magnesium, strontium, barium and/or molybdenum is contacted with the support material and then dried and heated, the latter under reducing conditions to form the finely dispersed promoted palladium catalyst.

The metal additive and palladium metal catalyst may be deposited concurrently or sequentially. That is, palladium may be codeposited with the metal additive of choice or it may be deposited upon the carrier either before or after such metal additive. Similarly, if more than one metal additive is used, the additives themselves may be deposited concurrently or in any desired sequence.

The palladium deposited is typically in metal form, desirably as fine discrete particles. The form of additive metal component is, however, not completely understood. It may be chemically associated with the palladium or it may be a physical admixture. For example, the additive may be alloyed with the palladium or not, in the form of a metal or an oxidized state of the metal, or it may be a silicate, carbonate, or the like.

Conditions of temperature, of pressure, and of gas composition are within the ranges that are essentially conventional for synthesis gas conversion to methanol for palladium catalysts. The reaction temperature markedly affects the productivity of the reaction with regard to methanol formation. Thus, an increase in reaction temperature results in an increased conversion to methanol with the proviso that the reaction pressure is correspondingly increased to avoid thermodynamic limitations. Increased pressure enhances the productivity of the reaction but may affect product distribution. Thus, for example, at increased pressures there may be an increased proportion of impurities, such as, ethanol and methyl formate in the product mixture. For purposes of economy, the reaction pressure is preferably within the range of 150-3,000 psia although a reaction pressure of from about 150-20,000 psia is generally suitable.

The operable space velocities in the flow reactor may vary from about 10² to 10⁶ per hour; space velocity being defined as volumes of reactant gas at 0° C. and 760 mm. mercury pressure, per volume of catalyst, per hour. Generally, the higher the space velocity, the more economical the overall reaction, although at excessively high space velocities the productivity of the reaction is adversely affected while excessively low space velocities cause the production of a more diverse spectrum of reaction products.

The molar ratio of hydrogen to carbon monoxide in the synthesis gas may vary extensively from about 1:10 to 10:1. The preferred hydrogen to carbon monoxide ratio is within the range of at least 1:5 to 5:1, a ratio of about 2:1 being most preferred. Increasing the percentage of hydrogen relative to carbon monoxide in the gas mixture increases the rate of the reaction, but adversely affects the economics of the overall process.

PREPARATION OF CATALYSTS

The catalysts cited in the examples below were all prepared by essentially the following sequence of steps: The desired quantities of palladium (II) chloride, ammonium paramolybdate, and the nitrate salts of lithium, magnesium, strontium and barium, depending upon the desired catalyst composition, were dissolved in a 1:1 HCl/H₂ O (by volume) solution at ambient temperature. The volume of solution was chosen to just fill the void volume (pores) of the support sample being impregnated. Davison™ Grade 59 silica gel (8-20 mesh--U.S. Sieves) was placed in a vacuum flask. The top of the flask was sealed with a rubber septum, and the flask was evacuated through the side arm. A syringe needle was then used to inject the solution onto the evacuated support. When addition was complete, the impregnated support was allowed to stand at one atmosphere for approximately 30 minutes. It was then carefully dried in a nitrogen atmosphere using the following sequence: 80° C. (for 1 hr.); 110° C. (2 hrs.); 150° C. (2 hrs.); and about 300° C. (2 hrs.). The dried, impregnated support was placed in a quartz tube through which hydrogen was continuously passed. The temperature was raised from 100° to 500° C., over a five hour period and then held at 500° C. for 1 hour. The reduced catalyst was then cooled to ambient temperature over a period of approximately two hours in a flowing hydrogen atmosphere and finally flushed with nitrogen before being removed.

In order to remove significant amounts of impurities which were present in the support material as received from the manufacturer, the Davison™ Grade 59 silica support was initially "washed" with oxalic acid prior to being used as the catalyst support. Such treatment consisted of passing a mixture of oxalic acid, glycerine, and water in proportions of 1:1.5:2.5 by weight, respectively, through a bed of support material (length/diameter ratio of about 20 to 25) contained within a glass tube which drained through a stopcock at its base. The contents of the tube were maintained at about 90° C. by means of resistance heating wire wrapped around the exterior of the tube. About 2.5 volumes of oxalic acid solution were used to wash one volume of 8-20 mesh silica gel over a three-hour period. The material was then washed with about six volumes of distilled water at 90° C. over a period of about four hours and then dried at 350° C. for about four hours.

The chemical analysis of the silica gel for iron, aluminum, sodium and calcium impurities following the abovedescribed treatment was as follows:

    ______________________________________                                         Iron as Fe.sub.2 O.sub.3                                                                           0.01% ± 0.004%                                          Aluminum as Al.sub.2 O.sub.3                                                                       0.01% ± 0.004%                                          Sodium as Na.sub.2 O                                                                               0.01% ± 0.004%                                          Calcium as CaO      0.02% ± 0.01%                                           ______________________________________                                    

DESCRIPTION OF TEST REACTOR

The reactor used in the following Examples was an internally silver-plated 316 stainless steel, bottom-agitated "Magnedrive" autoclave with a centrally positioned catalyst basket and a side product effluent line. It is of the type depicted in FIG. 1 of the paper by Berty, Hambrick, Malone and Ullock, entitled "Reactor for Vapor-Phase Catalytic Studies", presented as Preprint 42E at the Symposium on Advances in High-Pressure Technology--Part II, Sixty Fourth National Meeting of the American Institute of Chemical Engineers (AIChE), at New Orleans, Louisiana, on March 16-20, 1969 and obtainable from AIChe at 345 East 47th. Street, New York, New York 10017. A variable speed, magnetically driven fan continuously recirculated the reaction mixture over the catalyst bed. The following modifications were found to facilitate operation:

1. Hydrogen feed gas was introduced continuously at the bottom of the autoclave through the well for the shaft of the Magnedrive agitator.

2. Carbon monoxide feed gas was introduced continuously through a separate port at the bottom of the autoclave, in order to avoid a hydrogen-rich zone in the autoclave.

Effluent gases were removed through a port in the side of the reactor. Condensable liquid products were removed from the exit stream in a brine-cooled condenser at ca. 5° to 10° C. and were collected in a holding tank under pressure. The non-condensable components of the exit stream were vented through a wet test meter at atmospheric pressure to determine their total volume. A rubber septum in the atmospheric pressure line permitted syringe sampling of the non-condensable gases. No external recycle was employed.

DESCRIPTION OF THE TEST PROCEDURE

The weight of a given volume of catalyst sample was determined and the sample was placed in the catalyst basket. The quantity of catalyst charged was from about 15 to about 50 cc. depending upon the particular sample. Silver-plated screens and thin layers of glass wool were placed above and below the catalyst bed to prevent circulation of solid fines. The catalyst basket was charged to the reactor, and the reactor then sealed. The sealed reactor and the process lines were pressure tested at operating pressure. Nitrogen, hydrogen, or a mixture of the two was used for this test.

When the reactor was shown to be leak free, pure hydrogen was passed through the reactor, and the temperature raised to about 240° C. The hydrogen and carbon monoxide flows were then adjusted at the desired molar ratio to give a total purge rate of approximately 500 STP* liters/hr. This corresponds to a space velocity of from about 10,000 to about 33,000 STP volumes of gas per volume of catalyst per hour depending upon the volume of catalyst charged in the particular example. The hydrogencarbon monoxide ratio was determined by gas chromatographic analysis of an effluent gas aliquot.

When the appropriate gas composition was obtained, the reactor temperature was raised to 300° C. A period from about 0.5 hour to about one hour was allowed for the reactor to reach a steady-state at this temperature. The liquid product trap was then drained, a wet test meter reading was taken, and the time was noted as the beginning of a run. During the course of a run, one or more effluent gas samples were analyzed for hydrogen, carbon monoxide, methane, C₂ and C₃ hydrocarbons, methanol, ethanol, methyl formate, dimethyl ether and acetaldehyde. At the end of a run, the liquid product was collected, and the volume of effluent gas was noted. The liquid product was analyzed by gas chromatography.

The results of the tests are shown in Tables I and II. Examples B to L of Table I demonstrate the effect of the various promoters on the rate of methanol production relative to the unpromoted catalyst of Example A.

Examples M to P of Table II demonstrate the efficacy of the invention with alpha and gamma alumina catalyst supports. In addition, the examples demonstrate that an increase in methanol productivity can be achieved in accordance with the invention by depositing the metal additive upon the support prior to the deposition of the palladium catalyst rather than concurrently therewith as in the examples of Table I.

                  TABLE I                                                          ______________________________________                                         METHANOL PRODUCTION DATA.sup.a FOR                                             SUPPORTED PALLADIUM CATALYSTS.sup.b                                            CONTAINING LITHIUM, MAGNESIUM,                                                 STRONIUM, BARIUM OR MOLYBDENUM                                                 EXAMPLE   PROMOTER    RATE TO METHANOL.sup.c                                   ______________________________________                                         A          None       9.2                                                      B         0.1% Li     16.3                                                     C         0.2% Li     19.3                                                     D         0.4% Li     11.2                                                     E         0.1% Mg     11.8                                                     F         0.2% Mg     16.8                                                     G         0.4% Mg     12.4                                                     H         0.2% Sr     20.2                                                     I         0.2% Ba     16.1                                                     J         0.69% Ba    15.3                                                     K         0.2% Mo     14.9                                                     L         2.0% Mo     28                                                       ______________________________________                                          .sup.a Catalyst were tested at 300° C. and a reaction pressure of       2,500 psia using a 1:1 molar ratio of H.sub.2 :CO synthesis gas                composition at a space velocity of 10,000 hr -1.                               .sup.b The catalyst consist of 5 weight percent Pd plus the indicated          weight percent of promoter supported on Davison® Grade 59 silica gel       support. The weight percent of each component is based on the weight of        the support.                                                                   .sup.c "Rate" is the rate of synthesis of methanol in pounds of product        per cubic foot of catalyst per hour.                                     

                  TABLE II                                                         ______________________________________                                         METHANOL PRODUCTION DATA.sup.a FOR 2.5 WEIGHT PER-                             CENT PALLADIUM CATALYSTS SUPPORTED ON ALPHA                                    OR GAMMA ALUMINA.sup.b                                                                                  RATE                                                  EXAMPLE  SUPPORT         TO METHANOL.sup.c                                     ______________________________________                                         M        α-Al.sub.2 O.sub.3                                                                      5.0                                                    N        α-Al.sub.2 O.sub.3 + 3% BaO.sup.d                                                       7.7                                                    O        γ-Al.sub.2 O.sub.3                                                                      1.7.sup.e                                              P        γ-Al.sub.2 O.sub.3 + 7.9% BaO.sup.d                                                     4.2.sup.e                                              ______________________________________                                          .sup.a Catalysts were tested at 300°  C. and a reaction pressure o      2,500 psia using a 1:1 molar ratio of H.sub.2 :CO synthesis gas                composition at a space velocity of 26,000 hr.sup.-1.                           .sup.b The supports of all four Examples were manufactured by Norton           Company.                                                                       .sup.c The rate of synthesis of methanol is expressed in pounds of produc      per cubic foot of catalyst per hour.                                           .sup.d Support was prepared by impregnating the alumina with an aqueous        solution of barium nitrate, drying and calcining in air at 500°  C      for two hours.                                                                 .sup.e The values of methanol production for Examples O and P comprise th      rate to methanol plus the rate of dimethyl ether calculated as methanol.       This assumes that dimethyl ether results from the dehydration of two           molecules of methanol at acid sites on the support.                       

What is claimed is:
 1. In a heterogeneous catalytic process for the production of methanol by the reaction of hydrogen and carbon monoxide in the presence of a palladium-containing catalyst at a temperature of from about 200° C. to about 400° C. and a pressure of from about 150 to about 20,000 psia, the improvement for enhancing the production of methanol which comprises effecting said reaction in the presence of a heterogeneous solid catalyst containing palladium in combination with a metal additive selected from the group consisting of lithium, magnesium, strontium, barium, molybdenum and mixtures thereof.
 2. The process of claim 1 wherein said catalyst is supported on silica gel.
 3. The process of claim 2 wherein the palladium concentration on the catalyst support is from about 2-5% by weight, of the catalyst support.
 4. The process of claim 1 wherein said metal additive comprises molybdenum.
 5. The process of claim 4 wherein the molybdenum concentration on the catalyst support is from about 0.2% to about 3.0% by weight of the catalyst support.
 6. The process of claim 1 wherein the reaction temperature is from about 250° C. to about 350° C. and the reaction pressure is from about 150 psia to about 3000 psia.
 7. The process of claim 1 wherein said gaseous mixture contains hydrogen and carbon monoxide in a volume ratio of from about 1:5 to about 5:1. 